G6-Epoxy G6E-P is a two component, electrically conductive epoxy for high performance bonding, sealing and coating. We use a proprietary mix of high-performance nanocarbon fillers to achieve superb electrical properties for a non-metallic, electrically-conductive epoxy. It can cure at room temperature or more rapidly at elevated temperatures. G6E-P has a thick, pasty consistency after mixing and bonds well to a wide variety of substrates including metals, composites, ceramics, and glass.
- Non-magnetic; carbon filled
- Low electrical resistivity: <10 Ω·cm
- Ultralight: density is less than 1.1 g/cm3
- Low-cost silver alternative
- Excellent gap-filling adhesive
TWO COMPONENT SYSTEM: Part A – Black paste, Part B – Black paste
THE MIX RATIO: 100 (Part A) to 50 (Part B) by weight.
CURING INSTRUCTIONS: Best results are obtained when product is cured at one of the following schedules:
- 24 hours @ 25°C/77°F
- 3 hours @ 80°C/176°F
- 45 min @ 150°C/302°F
POT LIFE: 2-3 hours
GLASS TRANSITION TEMPERATURE: 62°C/153°F
MIXED VISCOSITY: 450-550 Pa·s at 25°C/77°F
HARDNESS, SHORE: >75 D
VOLUME RESISTIVITY: <10 Ω·cm
DENSITY: Part A 1.0 -1.2 g/cm3
Part B 1.0 -1.1 g/cm3
STORAGE & SHELF LIFE: 12 months at 25°C/77°F in unopened, unmixed containers. Stores and ships at room temperature. No freezing or dry ice required.
MIXING INSTRUCTIONS: Add Part B to Part A in a separate container and mix slowly until uniform. Vacuum degassing is recommended.
SAFETY & HANDLING: Always read the SDS for both Part A and Part B before use. Use the product with adequate ventilation. Keep away from sparks and open flames. Avoid prolonged contact with skin and breathing of vapors. Wash with soap and water to remove it from the skin.
PACKAGING: Part A (packaged in a jar) and Part B (packaged in a jar). G6E-P can be also packaged in various sizes and units to accommodate customer's requirements. Available in bulk size.